Silica Blanket |
| |
|
Characteristics |
| |
- Non-combustibility, high stable chemical properties, excellent insulation material
- High recovery rate after compression, shock and vibration resistance
- Enormous number of minute air spaces, making it excellent sound absorption
- Low shrinkage at high temperature, the shrinkage of HASI type at 1000°C is max. 1%
- Low thermal conductivity, excellent thermal insulation material
- Max. service temperature, ASI type, HASI type--1100°C
- After forming pipe, excellent resistance for wind velocity
|
|
| |
| The Main Application |
| |
- Steelworks, Aluminum industry, petro-chemical industry
- Furnace industry: thermal insulation for duct
- Machinery, household appliances: thermal insulation material
- Autos and motorcycles: thermal and acoustical insulation material for exhaust pipe, muffler
|
| |
| Chemical Properties of Silica Blanket |
| |
|
Density |
170 kg/m3 (10.6 lb/ft3) |
|
Physical behavior |
safe |
|
Toxicological behavior |
harmless |
|
Thermal stability |
1000°C 24hr |
|
Vibration behavior |
resistant to vibration | |
| |
| Thermal Properties of Silica Blanket |
| |
| Average temperature [°C] |
400 |
500 |
600 |
700 |
800 |
900 |
1000 |
1100 |
| Thermal Conductivity [W/m.K] |
0.06552 |
0.07622 |
0.08766 |
0.09675 |
0.12365 |
0.15325 |
0.18426 |
0.20051 | |
| |
| Heat Shrinkage of Silica Blanket |
| |
| Average temperature [°C] |
650 |
850 |
950 |
1050 |
| Shrinkage [max %] |
3.5 |
5.5 |
6.0 |
7.0 | |
| |
| Measurements of Silica Blanket |
| |
|
Thickness |
1/8" ~ 1" |
|
Width |
12" ~ 78" |
|
Length |
32" ~490?/DIV> |
Data are average results of test conducted under standard procedures and are subject to variation. Results should not be used for specification purposes.
Note: A material safety data sheet is available upon request.
The information, recommendations and opinions set forth herein are offered solely for your consideration, inquiry and verification, and are not, in part or total, to be construed as constituting a warrant or representation for which we assume legal responsibility. Nothing contained herein is to be interpreted as authorization to practice patented invention without a license. | |
|
|