Expandable Ceramic Fiber Paper |
|
|
TaoFibre ceramic fiber expandable paper is produced from a mixture of high purity ceramic fiber, natural graphite fine flakes, and organic binders through a fiber washing process. At about 1200 F (649 C), the paper expands up to maximum of 400% of its thickness. This feature serves as excellent material for gasket and sealing applications.
Typical Applications:
- High temperature gasketing and sealing
- Expansion joint insulation
- Fire protection
- Industrial furnace seals
- Aluminum filtering bowl edge sealing
|
 | |
Physical Properties |
| |
|
Color
|
Gray
|
|
Maximum temperature rating,°F
|
2300
|
|
Continuous use limit,°F
|
2100
|
|
Melting point,°F
|
3100
|
|
|
|
Chemical Content
|
Silica, SiO2 |
45-48 |
|
Alumina Oxide, Al2O3 |
42 |
|
Carbon, C |
15-Oct |
|
Other |
2 |
|
Organic Binder |
10-May |
|
Tensile Strength |
|
16-18 pcf. density |
0.5-0.7 Mpa |
|
|
|
|
Expansion, % increase |
|
@ 400 °F |
90 ( from
1/8” thickness) |
|
@ 1800 °F |
420 ( from 1/8” thickness) |
|
@ 1800 °F |
320 ( from 1/8” thickness) |
|
|
|
|
Sizes Available |
24", 48" |
|
Thickness |
1/8", 1/16" |
|
| Data are avarage results of test conducted under standard procedures and are subject to variation. Results should not be used for specification purposes. Note: A material safety data sheet is available upon request. The information, recommendations and opinions set forth herein are offered solely for your consideration, inquiry and verification, and are not, in part or total, to be construed as constituting a warrant or representation for which we assume legale responsibility. Nothing contained herein is to be interpreted as authorization to practice patented invention without a license. |
| |
|
|